TiC-FeCrMo cermets have been obtained in fully dense form by Sinter HIP at 1400 degrees C. Significant microstructural changes have been observed in these materials for relatively small variations in their carbon content after sintering. In the cermets with higher carbon content Cr-rich likely M7C3 carbides are observed to precipitate at the (Ti1-x,Mo-x)(y)C-z - metal interface. In addition, these cermets present a significant amount of retained austenite as part of the metal matrix. No retained austenite and many fewer M7C3 carbides are found in alloys with a reduction of 0.2 wt% in the total C content. Continuous cooling diagrams have been obtained from an austenitizing temperature of 950 degrees C. Hardness increases by 30% with respect to that of as sintered specimens after cooling at 1 degrees C/s confirming that these TiC-FeCrMo cermets are suitable for hardening by air-quenching. At this cooling rate, it is observed that the relatively small carbon changes mentioned before have a significant effect on the bainitic transformation, displacing its onset to higher temperatures as the C content is reduced. Slower cooling rates result in complex microstructures, in which, in addition to martensite, ferritic bainite, M7C3 and M23C6 carbides are also found. Microstructure and hardness of TiC-FeCrMo materials can be modified by the use of standard heat treatments to obtain a wide variety of mechanical properties suitable for certain hot rolling applications.

Recrystallization and grain growth during plate rolling are prevented by Nb addition both with the solute drag and the Nb carbide precipitation. Although a fine microstructure is achieved in the base material, welding heat completely changes the microstructure in the heat affected zone (HAZ). In this study, laboratory simulation of the coarse grain HAZ (CGHAZ) thermal cycle of double submerged arc welded linepipe was carried out using low carbon steels containing different Nb contents. Extraction residue analysis of the simulated CGHAZ samples revealed that almost all the Nb remained in solid solution. To clarify the interaction of Nb carbide dissolution and grain growth on overall simulated HAZ microstructure evolution, additional weld HAZ thermal simulations were performed. It was found that Nb carbides remain undissolved at HAZ peak temperatures up to 1 200 & DEG;C and showed significant pinning effect to prevent austenite grain growth. Significant grain growth was seen after continuous fast heating to 1 350 & DEG;C peak temperature, while the higher Nb added steel showed a slower overall austenite grain growth rate, suggesting that grain growth in the HAZ at higher temperature was suppressed by the combined effects of slower coarse Nb carbide dissolution providing some pinning, and the solute drag effect of higher amounts of Nb in solid solution. A pronounced retardation of longer-term isothermal grain growth was identified at 1 350 & DEG;C at higher levels of solute Nb, confirming the influence of Nb solute drag on high temperature resistance to austenite grain coarsening.

Obtaining high levels of mechanical properties in steels is directly linked to the use of special mechanical forming processes and the addition of alloying elements during their manufacture. This work presents a study of a hot-rolled steel strip produced to achieve a yield strength above 600 MPa, using a niobium microalloyed HSLA steel with non-stoichiometric titanium (titanium/nitrogen ratio above 3.42), and rolled on a Steckel mill. A major challenge imposed by rolling on a Steckel mill is that the process is reversible, resulting in long interpass times, which facilitates recrystallization and grain growth kinetics. Rolling parameters whose aim was to obtain the maximum degree of microstructural refinement were determined by considering microstructural evolution simulations performed in MicroSim-SM (R) software and studying the alloy through physical simulations to obtain critical temperatures and determine the CCT diagram. Four ranges of coiling temperatures (525-550 degrees C/550-600 degrees C/600-650 degrees C/650-700 degrees C) were applied to evaluate their impact on microstructure, precipitation hardening, and mechanical properties, with the results showing a very refined microstructure, with the highest yield strength observed at coiling temperatures of 600-650 degrees C. This scenario is explained by the maximum precipitation of titanium carbide observed at this temperature, leading to a greater contribution of precipitation hardening provided by the presence of a large volume of small-sized precipitates. This paper shows that the combination of optimized industrial parameters based on metallurgical mechanisms and advanced modeling techniques opens up new possibilities for a robust production of high-strength steels using a Steckel mill. The microstructural base for a stable production of high-strength hot-rolled products relies on a consistent grain size refinement provided mainly by the effect of Nb together with appropriate rolling parameters, and the fine precipitation of TiC during cooling provides the additional increase to reach the requested yield strength values.

This work has focused on the study of hot working behavior of boron high strength steels microalloyed with different combinations of Nb and/or Mo. The role of Nb and Mo during the hot deformation of low carbon steels is well known: both mainly retard austenite recrystallization, leading to pancaked austenite microstructures before phase transformation and to refined room temperature microstructures. However, the design of rolling schedules resulting in properly conditioned microstructures, requires microstructural evolution models that take into account the effect of the different alloying elements. In this specific case, the effect that high levels of molybdenum (0.5 pct) have in the recrystallization delay was evaluated. In that respect, hot torsion tests were performed in this work to investigate the microstructural evolution during hot deformation of four boron steels, with different Nb (0.025 pct) and Mo (0.5 pct) combinations. The retardation in recrystallization kinetics was modeled in all cases and measured kinetics agree with those predicted by equations previously developed for Nb-Mo microalloyed steels with lower Mo concentrations (< 0.3 pct). The strain-induced precipitation in the Nb and Nb-Mo bearing steels was also characterized. Finally, the fractional softening evolution during multipass rolling simulations was compared with MicroSim (R) model predictions, showing a good agreement with experimental results. (C) The Author(s) 2022

The dynamic recrystallization behavior of ultra-high strength boron-microalloyed steels optionally alloyed with niobium and molybdenum is analyzed in this paper. Multipass torsion tests were performed to simulate plate rolling conditions followed by direct quenching. The influence of alloy composition on the transformed microstructure was evaluated by means of EBSD, thereby characterizing the morphology of the austenite grain morphology after roughing and finishing passes. The results indicated that for Nb-microalloyed steel, partial dynamic recrystallization occurred and resulted in local clusters of fine-sized equiaxed grains dispersed within the pancaked austenitic structure. A recrystallized austenite fraction appeared and transformed into softer phase constituents after direct quenching. The addition of Mo was shown to be an effective means of suppressing dynamic recrystallization. This effect of molybdenum in addition to its established hardenability effects hence safeguards the formation of fully martensitic microstructures, particularly in direct quenching processes. Additionally, the circumstances initiating dynamic recrystallization were studied in more detail, and the interference of the various alloying elements with the observed phenomena and the potential consequences of dynamic recrystallization before quenching are discussed.

Intercritically deformed steels present combinations of different types of ferrite, such as deformed ferrite (DF) and non-deformed ferrite (NDF) grains, which are transformed during the final deformation passes and final cooling step. Recently, a grain identification and correlation technique based on EBSD has been employed together with a discretization methodology, enabling a distinction to be drawn between different ferrite populations (NDF and DF grains). This paper presents a combination of interrupted tensile tests with crystallographic characterization performed by means of Electron Backscatter Diffraction (EBSD), by analyzing the evolution of an intercritically deformed micro-alloyed steel. In addition to this, and using the nanoindentation technique, both ferrite families were characterized micromechanically and the nanohardness was quantified for each population. NDF grains are softer than DF ones, which is related to the presence of a lower fraction of low-angle grain boundaries. The interrupted tensile tests show the different behavior of low- and high-angle grain boundary evolution as well as the strain partitioning in each ferrite family. NDF population accommodates most of the deformation at initial strain intervals, since strain reaches 10%. For higher strains, NDF and DF grains behave similarly to the strain applied.

Recently, advanced thermomechanical hot rolling schedules followed by direct quenching are being developed in order to avoid reheating and quenching treatment after hot rolling to eliminate an energy and cost consuming step. The use of boron as an alloying element is a widely known practice in high strength medium carbon steels to increase the strength due its potential for delaying phase transformation and improving hardenability. In addition, a significant synergetic effect on hardenability could be reached combining B with microalloying elements (adding Nb, Mo or Nb-Mo). With the purpose of exploring the effect of microalloying elements and thermomechanical rolling schedule, laboratory thermomechanical simulations reproducing plate mill conditions were performed using ultra high strength steels micro-alloyed with Nb, Mo, and Nb-Mo. To that end, plane compression tests were performed, consisting of an initial preconditioning step, followed by several roughing and finishing deformation passes and a final quenching step. After fast cooling to room temperature, a tempering treatment was applied. In the present paper, the complex interaction between the martensitic microstructure, the tempering treatment, the addition of microalloying elements, and the resulting tensile properties was evaluated. For that purpose, an exhaustive EBSD quantification was carried out in both quenched as well as quenched and tempered states for all the steel grades and the contribution of different strengthening mechanisms on yield strength was analyzed. Highest tensile properties are achieved combining Nb and Mo, for both quenched (Q) and quenched and tempered states (Q&T), reaching yield strength values of 1107 MPa and 977 MPa, respectively. Higher tempering resistance was measured for the Mo-bearing steels, making the CMnNbMoB steel the one with the lowest softening after tempering. For CMnB grade, the yield strength reduction after tempering of about 413 MPa was measured, while for NbMo micro-alloyed steel, yield strength softening is considerably reduced to 130 MPa.

The application of direct quenching after hot rolling of plates is being employed in the production of ultra-high-strength hot rolled plates. When heavy gauge plates are produced, the complexity involve in achieving high cooling rates in the plate core is increased and the formation of undesirable soft phases within martensite is common. In the current paper, both direct quenching and conventional quenching (DQ and CQ) processing routes were reproduced by dilatometry tests and continuous cooling transformation (CCT) diagrams were built for four different high-strength boron steels. The results indicate that the addition of Mo and Nb-Mo suppresses the ferritic region and considerably shifts the CCT diagram to lower transformation temperatures. The combination of DQ strategy and the Mo-alloying concept provides the best option to ensure hardenability and the formation of a fully martensitic microstructure, and to avoid the presence of soft phases in the center of thick plates.

The synergetic effect on hardenability by combining boron with other microalloying elements (such as Nb, Mo and Nb + Mo) is widely known for high-strength medium carbon steels produced by direct quenching and subsequent tempering treatment. The improvement of mechanical properties could be reached through optimization of different mechanisms, such as solid solution hardening, unit size refinement, strain hardening, fine precipitation hardening and the effect of carbon in solid solution. The current study proposes a procedure for evaluating the contribution of different microstructural aspects on Charpy impact toughness. First, the effect that austenite conditioning has on low-temperature transformation unit sizes and microstructural homogeneity was analysed for the different microalloying element combinations. A detailed crystallographic characterization of the tempered martensite was carried out using electron backscattered diffraction (EBSD) in order to quantify the effect of unit size refinement and dislocation density. The impact of heterogeneity and presence of carbides was also evaluated. The existing equations for impact transition temperature (ITT50%) predictions were extended from ferrite-pearlite and bainitic microstructures to tempered martensite microstructures. The results show that microstructural refinement is most beneficial to strength and toughness while unit size heterogeneity has a particularly negative effect on ductile-to-brittle transition behaviour. By properly balancing alloy concept and processing, steel having a yield strength above 900 MPa and low impact transition temperature could be obtained by direct quenching and tempering.

The mechanical properties of intercritically rolled microstructures have been scarcely reported in literature. Although the strengthening effect of intercritical rolling is generally recognized, there is no a clear opinion on its effect on toughness. Therefore, a greater knowledge of how different process parameters affect the mechanical properties during intercritical deformation is required. With the aim of evaluating the relationship between microstructure and mechanical properties on intercritically deformed low carbon steels, plane strain compression tests were carried out. Plane strain compression tests allow for both the characterization of the microstructural features and the evaluation of mechanical properties, via tensile and Charpy tests. Firstly, the intercritically deformed microstructures were characterized using the EBSD technique, and then a discretization methodology was used to distinguish both intercritically deformed and non-deformed ferrite populations. Next, strength and toughness properties were measured by means of tensile and Charpy tests. The results indicate that the reduction of the deformation temperature leads to an increment of yield strength for both steels, but at the same time toughness properties worsen. Deformed ferrite fractions higher than 25% result in a very pronounced loss of ductility. The yield strength was predicted by estimating the contribution of different strengthening mechanisms (solid solution, grain size refinement, dislocation density) corresponding to each ferrite population by considering a nonlinear law of mixtures. Similarly, the impact of different microstructural parameters (solid solution, grain size, microstructural heterogeneity, contribution of dislocation density and secondary phases) on toughness was evaluated and a new equation able to predict ductile to brittle transition temperature for intercritically deformed microstructures was developed.

Final Report RFSR-CT-2013-00007

Three main topics are covered in this paper regarding Nb-Mo interactions in microalloyed steels. First, the synergistic behavior of Nb and Mo in enhancing solute drag effects and modifying recrystallization and precipitation kinetics in austenite under hot working conditions is analyzed. Then, the effect of different microalloying additions on the final phase transformations is examined. In addition to composition and austenite conditioning effects on the phases formed and the corresponding CCT diagrams, a quantitative study using an EBSD technique is described which was performed in order to measure unit size distributions and homogeneity of complex microstructures. Finally, the contribution of different strengthening mechanisms to yield strength is evaluated for different coiling temperatures and compositions.